ASTM 310/310S Stainless H beam steel are typically used for elevated temperature applications. Stainless steel 310/310S Stainless H beam steel is an austenitic heat resistant alloy with excellent resistance to oxidation under mildly cyclic conditions through 2000ºF. Its high chromium and nickel contents provide comparable corrosion resistance, superior resistance to oxidation and the retention of a larger fraction of room temperature strength than the common austenitic alloys like Type 304. Stainless 310 H beam is often used at cryogenic temperatures, with excellent toughness to -450°F, and low magnetic permeability.

ASTM 310/310S Stainless H beam steel Chemical composition %

Chemical Composition 310 310S
Carbon 0.25 max 0.08 max
Manganese 2.00 max 2.00 max
Silicon 1.50 max 1.50 max
Phosphorus 0.045 max 0.045 max
Sulphur 0.030 max 0.030 max
Chromium 24.00 - 26.00 24.00 - 26.00
Nickel 19.00 - 22.00 19.00 - 22.00

stainless steel 310/310S Stainless H beam steel Mechanical Properties

Mechanical Properties 310/ 310S
Grade 0.2 % Proof Stress MPa (min) 205
Tensile Strength MPa (min) 520
Elongation % (min) 40
Hardness (HV) (max) 225

stainless steel 310/310S H beam is readily fabricated by standard commercial procedures. In comparison to carbon steel, stainless steels are tougher and tend to work harden rapidly. Katalor will return you with high-quality products and complete after-sale service with the lowest price. Any need in stainless steel 310/310S H beam , you can contact us!