SS400 angle steel size and specification standards

SS400 angle steel is a general structural steel commonly used in construction, machinery manufacturing and other fields. The following is a detailed overview of SS400 angle steel:

Material: The main component of SS400 angle steel is carbon steel, which complies with JIS G3101 standard. SS400 belongs to the Japanese steel standard. Its chemical composition includes carbon content less than 0.22%, silicon content less than 0.35%, manganese content less than 1.40%, phosphorus content less than 0.045%, and sulfur content less than 0.050%.

Features: It has good weldability, processability and mechanical properties, and is easy to cut, shape and weld.

Usage: Widely used in building structures, bridges, machinery manufacturing, shipbuilding and other fields, such as beams, columns, frames, supports and other structural components.

Specifications: Usually described in terms of thickness and width, common sizes are 20x20mm to 200x200mm, and the thickness range is generally 2.0mm to 12mm.

Standard: Comply with the Japanese industrial standard JIS G 3101 and meet the relevant mechanical properties, chemical composition and dimensional deviation requirements.

SS400 angle steel is a common building material with the following size and specification standards:

- Specifications: Usually described in terms of thickness and width, such as 2.5mm x 25mm.
- Size range: Common sizes are 20x20mm to 200x200mm.
- Thickness range: Thickness usually ranges from 2.0mm to 12mm.

Specific SS400 angle steel sizes and specifications may vary by manufacturer and region, it is recommended to contact your local supplier for accurate information based on specific needs.
It should be noted that before specific use, please confirm that the product meets the relevant standards and requirements in your region.